This dataset is a market dataset, representing the consumption market of the region; the dataset includes the transport of the product from the gate to the consumer end, and the transport service is calculated according to the transport situation of this product in this region. This dataset represents pellets pressed from ferrosilicon and calcined dolomite after mixing and ball milling, mainly composed of MgO and CaO, with uniform composition and stable proportions. They are mostly ellipsoidal spheres of 40–50 mm, with a dense structure and moderate strength, not easily pulverised during transport and furnace loading, while also having good air permeability and mechanical stability. The key upstream starting raw materials of the product are calcined dolomite and ferrosilicon; downstream, it is a key raw material entering the reduction process in the Pidgeon process for magnesium smelting. The dataset contains the main raw and auxiliary materials, energy and waste of the production process, and infrastructure such as the manufacture of production equipment and the construction of plant buildings is not included within the dataset boundary; the data inventory is formed by merging data from multiple sources.
Activity Description
The entire production process includes batching, grinding, and pelletizing. The entire process covers the process from ferrosilicon and whitening to pelletization.
Process Description
The pellets, produced by mixing ferrosilicon and calcined dolomite followed by ball milling and pressing, are mainly composed of MgO and CaO, with uniform composition and stable proportions. They are generally elliptical spheres of 40 to 50 mm, with a dense structure and moderate strength, which prevents pulverization during transportation and furnace charging. They also exhibit good gas permeability and mechanical stability. Since the raw materials are finely ground, the pellets have high reactivity and can fully react with the reducing agent under vacuum thermal reduction conditions, making them a key intermediate product that enters the reduction process in the Pidgeon process for magnesium production.
Time period
2023
2026
Geography
China,Gansu
Macroeconomic value
Business-as-Usual
Data validation
Yes
Technology
Current Technology
Technology comment
The ferrosilicon is crushed into coarse particles of about 3~8mm by the jaw crusher, mixed according to the ratio of calcined dolomite: ferrosilicon = 100:21, and then the mixture is sent to the ball mill for grinding until the particle size reaches 200 mesh. The ground powder is transported to the briquetting machine through a bucket elevator, and is extruded into elliptical spheres of about 40 to 50mm at a pressure of 9.8~29.4MPa. The spheres and powder smaller than 40mm are screened and returned to the briquetting machine, and the qualified spheres are sent to the reduction workshop.