This process refers to the production activity of producing 1 kg of low-carbon ferromanganese by the electro-silicothermic process. Low-carbon ferromanganese is an alloy material with manganese and iron as its main components and a carbon content not exceeding 0.7%. As the most widely used deoxidizer and alloy additive in the steelmaking industry, it can improve the hardness, ductility, and wear resistance of steel. The dataset includes raw and auxiliary materials such as manganese ore, silicomanganese alloy, electrodes, and limestone, and inputs of energy and energy media such as electricity and water; the outputs include the product medium-carbon ferromanganese, the wastes slag and dust-collection ash (which can be recovered to cement plants for comprehensive utilization), as well as emissions to water bodies and the atmosphere. The data inventory is formed by merging data from multiple sources, and the data representativeness is optimized using industry standards such as the 3140 Ferroalloy Industry Coefficient Handbook.
Activity Description
Low-carbon ferromanganese is produced using silicon-manganese alloy, manganese ore, and limestone as raw materials, using a refining furnace (electric silicothermal method). During the heating process of the charge in the charge area, the silicon in the silicon-manganese alloy is mainly used as a reducing agent to reduce the MnO obtained from the manganese ore. The silicon is oxidized to achieve the purpose of refining and desiliconization. After the silicon in the alloy is reduced to the specified limit, low-carbon ferromanganese with a carbon content similar to that of the silicon-manganese alloy is obtained. The overall process flow mainly includes arcing and arcing of the refining furnace - feeding (manganese ore, lime) - melting of raw materials - adding silicon-manganese alloy (liquid) - refining - tapping.
Process Description
Low-carbon ferromanganese is an alloy material with manganese and iron as its main components. The carbon content does not exceed 0.7%. As the most widely used deoxidizer and alloy additive in the steelmaking industry, it can improve the hardness, ductility and wear resistance of steel.
Time period
2023
2026
Geography
China
Macroeconomic value
Business-as-Usual
Data validation
Yes
Technology
Current Technology
Technology comment
Using silicon-manganese alloy, manganese ore, and limestone as raw materials, it is produced using a refining furnace (electric silicothermal method)-hot charging process, which is a method widely used at home and abroad. During the heating process of the charge in the charge area, the silicon in the silicon-manganese alloy is mainly used as a reducing agent to reduce the MnO obtained from the manganese ore. The silicon is oxidized to achieve the purpose of refining and desiliconization. After the silicon in the alloy is reduced to the specified limit, medium/low carbon ferromanganese with a carbon content similar to that of the silicon-manganese alloy is obtained.